选取海阳海砂、淡化海阳海砂和河砂三种细骨料,分别制备强度等级为C30和C50的混凝土,进行加速碳化与氯离子侵蚀复合试验的研究,测出混凝土试块不同深度的水溶性自由氯离子含量.结果表明:海砂混凝土、淡化海砂混凝土在碳化与氯离子侵蚀复合作用下的破坏规律与河砂混凝土基本一致.碳化时间对各种混凝土中氯离子的扩散影响都很大.混凝土强度等级,海砂中固有的氯离子等因素也影响混凝土各深度的水溶性自由氯离子含量.
Abstract：Three kinds of sand are selected to make concrete specimens with strength classes of C30 and C50,which are natural sea sand,washed sea sand and river sand from Haiyang City.After the experiment of accelerated carbonation and chloride penetration,the free chloride content of concrete at different depth is measured.Conclusion can be made that the specimens made of three kinds of sand degrade have almost the same rule under the invading of both accelerated carbonation and chloride penetration.The time of carbonation has great influence on chloride penetration in all kinds of concrete specimens.The concrete strength classes and intrinsic chloride content of sea sand influence the chloride content of concrete at different depth as well.
[1]王威.海砂资源现状及其采矿权延续申请的程序相关问题[J].国土资源情报,2006(5):43-46.WANG Wei.The Current Situation of Sea Sand Resources and ProgramProblemabout Continue Apply for Mining Right[J].Journalof Territorial Resources,2006(5):43-46.
[2]Vladi mír ivica.Corrosion of Reinforced Induced by Environment Containing Chloride and Carbon Dioxide[J].Bull Mater Sic,2003,26(6):605-608.
[3]Anstice DJ,Page C L,Page M M.The Pore Solution Phase of Carbonated Cement Pastes[J].Cement and Concrete Research,2005,35(2):377-383.
[4]柳俊哲.混凝土碳化研究与进展(3)——腐蚀因子的迁移[J].混凝土,2006(1):12-17.LI UJun-zhe.A Review of Carbonation in Reinforced Concrete(Ⅲ):Migration of Corrosive Factors in Concrete[J].Concrete,2006(1):12-17.
[5]Gonzalez J A,Feliu S,Rodriguez P,et al.Some Question on the Corrosion of Steel in Concrete-Part 1:When,Howand How MuchSteel Corrodes[J].Materials and Structures,1996(29):40-46.
[6]金祖权,孙伟,李秋义.碳化对混凝土中氯离子扩散的影响[J].北京科技大学学报,2008,30(8):921-925.JI N Zu-quan,SUN Wei,LI Qiu-yi.Effect of Carbonation on Chloride Diffusionin Concrete[J].Journal of University of Science andTechnology Beijing,2008,30(8):921-925.
[7]颜承越.混凝土碳化与强度关系的建立与应用[J].混凝土与水泥制品,1993(6):19-21.YAN Cheng-yue.The Founding and Usage of Relation Between Carbonation and Strength[J].China Concrete and Cement Products,1993(6):19-21.
[8]白轲,杨元霞.碳化作用对混凝土强度及氯离子渗透性能的影响[J].粉煤灰综合利用,2008(6):23-26.BAI Ke,YANG Yuan-xia.Effects of Carbon Dioxide on Compressive Strength and Chloride Penetration of Concrete[J].Fly AshComprehensive Utilization,2008(6):23-26.
基本信息:
中图分类号:TU528
引用信息:
[1]巴光忠,苏卿,赵铁军,等.碳化对海砂混凝土中氯离子扩散的影响[J].青岛理工大学学报,2011,32(02):18-22.
基金信息:
“十一五”科技支撑计划项目(2006BAJ02B04)
2011-04-15
2011-04-15